THE EFFECT OF ALLOYING ADDITIVES AND PROCESS PARAMETERS ON THE SOLIDIFICATION CHARACTERISTICS OF THE ALUMINIUM ALLOY AlSi7Mg0.3
Abstract
We have investigated the aluminium alloy AlSi7Mg0.3, which is used in the production of castings. Melting was carried out in an electric resistance furnace. Casting was done into measuring cells with thermocouples for simple thermal analysis. Six samples that differed in terms of the additives used for grain refinement and inoculation, with two different holding times, were cast. An alloying material AlTi5B1 was used for grain refinement. The inoculation effect on the solidification was studied with the addition of the inoculant AlSr10. The temperature of the melt in the furnace was 750 °C and the melting time was one hour and ten minutes. Firstly, the samples were cast, the melt was cooled, solidification occurred and finally it was cooled down in the solid state. During the entire cooling process, the temperature as a function of time was measured and the cooling curves were obtained. After the casting, samples for metallographic inspection were prepared. The cooling curves show that in samples with a longer holding time, the additions of either the inoculant or the grain refinement agent, had a better effect. This is evident with a higher maximum liquidus temperature TLmax in sample Ti10 and lower maximum eutectic temperature TE1max in sample Sr10 in comparison to the basis alloy. The same we can conclude from the microstructure analysis of the samples. The samples with inoculant and with a longer holding time, possessed a finer eutectic structure (αAl+βSi), than the samples with the shorter holding time. The same applies for the samples with grain-refinement additions. The estimated grain sizes were smaller in the sample with the longer holding time.
References
2 L. Kuchariková, T. Liptáková, E. Tillová, D. Kajánek, E., Schmidová, Role of Chemical Composition in Corrosion of Aluminum Alloys, Metals, 8 (2018) 581–594, doi:10.3390/met8080581
3 M. Vončina, P. Mrvar, J. Medved, Thermodynamic Analysis of AlSiMg Alloy, RMZ- Materials and Geoenviroment, volume 52, 3 (2006) 621–633
4 M. B. Djurdjevic, I. Vicario, G. Huber, Review of Thermal Analysis Applications in Aluminium Casting Plants, Rev. Metal. 50 (2014) (1): e004. doi: http://dx.doi.org/10.3989/revmetalm.004
5 A. A. Canales, J. Talamantes-Silva, D. Gloria, S. Valtierra, R. Colas, Thermal analysis during solidification of cast Al-Si alloys, Thermochim. Acta 510 (1–2) (2010) 82–87, http://dx.doi.org/10.1016/j.tca.2010.06.026
6 E. Kantoríková, M. Kuriš, R. Pastirčák, Heat Treatment of AlSi7Mg0.3 Aluminium, Alloys with Increased Zirconium and Titanium Content, Archives of foundry engieering, volume 21, 2 (2021) 89–93
7 F. Zupanič, S. Žist, M. Albu, I. Letofsky-Papst, J. Burja, M. Vončina, T. Bončina, Dispersoids in Al-Mg-Si alloy AA 6086 modified by Sc and Y, Materiali, 16(8) (2023) 2949, https://doi.org/10.3390/ma16082949
8 B. Friedrich, M. Gökelm, Understanding of Inclusions - Characterization, Interactions and Boundaries of Removability with Special Focus on Aluminium melts, Dresden, September 2015, doi: 10.13140/RG.2.1.4945.3200/1
9 M. Faraji, L. Katgerman, Microstructural analysis of modification and grain refinement in a hypoeutectic Al–Si alloy, International Journal of Cast Metals Research, volume 22, 1 (2009) 108–110, doi:10.1179/136404609X367461
10 L. Bäckerud, E. Król, J. Tamminen: Solidification characteristic of aluminium alloys: wrought alloys, Skanaluminium, Oslo, 1986, 30–36
11 M. Petrič, J. Medved, P. Mrvar, Effect of the grain refinement, modification and the cooling
rate on microstructure of the AlSi10Mg alloy, RMZ - Materials and Geoenvironment, volume 53, 3 (2006) 385–401
12 J. Mrvar, Karakterizacija zlitin Al-Zn-Mg-Cu. Diplomsko delo. Univerza v Ljubljani, 2020
13 M. Vončina, G. Hvala, J. Medved, B. Žužek, M. Petrič, Determination of material quality by methods of thermal analysis, RMZ- Materials and Geoenviroment, volume 68, 2 (2022) 1–9, doi:10.2478/rmzmag-2021-0006
14 Alloy Standards, EN 1706: Compare the properties of all alloy grades /numbers
[online, cited 2023-10-10]. Available on:
http://www.steelnumber.com/en/standard_alloy_eu.php?gost_number=1706
15 A. Knaislová, Š. Michna, I. Hren, T. Vlach, A. Michalcová, P. Novák, D. Stančeková, Microstructural Characteristics of Al-Ti-B Inoculation Wires and Their Addition to the AlSi7Mg0.3 Alloy, Materials, 15 (21) (2022) 7626, https://doi.org/10.3390/ma15217626
16 M. S. Agnes, S. Ehab, V. Songmene, S. H. Fawzy, A Comparative Study of Grain Refining of Al-(7–17%) Si Cast Alloys Using Al-10% Ti and Al-4% B, Master Alloys Materials 16 (17) (2023), 2867, https://doi.org/10.3390/ma16072867
17 L. Kuchariková, E. Tillová, M. Chalupová, M. Mazur, A. Herčko, R., Čička, Analysis of microstructure in AlSi7Mg0.3 cast alloy with different content of Fe, Transportation Research Procedia, 40 (2019) 59–67, https://doi.org/10.1016/j.trpro.2019.07.011
18 R. Martinez, I. Guillot, D. Massinon, New heat treatment to improve the mechanical properties of low copper aluminum primary foundry alloy, Materials Science and Engineering: A, volume 755, 7 (2019) 158–165, https://doi.org/10.1016/j.msea.2019.04.001
19 A. Bűhrig-Polaczek, E. Schaberger-Zimmermann, S. Fischer, V. Groten, B. Bӧttger, J. Eiken, Metallurgy, solidification parametrs and microstructure of cast Al-alloys. Livarski vestnik, volume 61, 1 (2014) 2–15
20 L. Bolzoni, N. Haribabu, Engineering the heterogeneous nuclei in Al-Si alloys for solidification control, Applied Materials Today, 5 (2016) 255–259, [online]. Available on: https://www.sciencedirect.com/science/article/pii/S2352940716301792
21 A. J. Dolata, M. Dyzia, S. Boczkal, Influence of the Sr and Mg alloying additions on the bonding between matrix and reinforcing particles in the AlSi7Mg/SiC-Cg hybrid composite, Arch. Metall. Mater., volume 61, 2 (2016) 651–656, doi: 10.1515/amm-2016-0111
22 J. Asensio-Lozano, G. Vander Voort, The Al-Si Phase Diagram. Solutions for Materials Preparation, Testing and Analysis. Published by Buehler, a division of Illinois Tool Works, volume 5, Issue 1 (2023), https://www.buehler.com/assets/solutions/technotes/vol5issue1.pdf.